EFFECT OF TRANSITION METAL Ni ON WELDING PROPERTIES OF TITANIUM ALLOY STAINLESS STEEL
Sun Ronglu1; Meng Xiangcai1 ;Zhang Jiuhai2

1.Second Department; Jiamusi Institute of Technology; Jiamusi 154007 ;
2.School of Materials Science and Engineering; Harbin Institute of Technology; Harbin 150001

Abstract:With increase of Ti alloys use in industry, weld of Ti alloys to steel becomes more and more impotant. Microstructures and properties of diffusion welded joint of TC 4 to 1Cr18Ni9Ti adding the transition metal Ni have been observed with microscopy, SEM, EPMA and tested by tensile tests, respectively. The results show that atom diffusion and migration between Ti and Fe or C are effectively prevented by adding pure Ni as transition metal and a film joint is obtained. The properties of welded joint depend on weld rate of Ti to stainless steel and the thickness of Ni Ti metallic compounds. The optimum weld parameters are as follows: weld temperature is 850 ℃, weld time is 5 min, weld specific stress is 10 MPa.

 

Key words: Ti alloy stainless steel transition metal Ni diffusion welding

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn