MICROSTRUCTURE AND PROPERTY OF Al/TIC COMPOSITES PREPARED BY REACTION SYNTHESIS
Zhang Erlin,Zeng Xiaochun,Zeng Songyan,Li Qingchun

School of Material Science and Engineering,Harbin Institute of Technology,Harbin 150001

Abstract:A novel in-situ process-Reaction Synthesis has been used to fabricate Al/TiC compas-ites,the phase constitute,microstructure and mechanical property of the Al/TIC composite have been investigated by the use of XRD and SEM. It has been shown that the reaction synthesized TiC paxticu-late is submicron in size(abaut 0. 1一0. 8μm),spherical in shape and smooth in surface. In macrostruc-tore the distribution of the TiC particulate in matrix is homogeneous。 Gut in micostructure there is mi-
cro-segregation of the TiC particulate at the intergrannular. The cast structure become fine because of the existence of the TiC particulate. In addition, with the increasing of weight percentage of TiC partic-ulateg.al in alloy,the yield strength and ultimate tensile strength of the composite increase significantly, e.g.at 15%TiC, 1I7% and 103% increase respectively, in the same time the elongation of the composite is still more than 4. 5%. In the end,the composite. The results show that the analysis has been done by SE1VI on the fracture morphology of the fracture is ductility, and mainly because of the cluster of TiC particulate to tntergrannular and the synthesis of bar morphology A13Ti.

 

Key words: composites    microstructure   mechanical property     particulate   reaction synthesis

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn