SIMULATING EXPERIMENTS OF HOT CORROSION CELL
Mu Daobin; He Yedong; Zhu Rizhang

Department of Surface Science and Corrosion Engineering; University of Science and Technology Beijing; Beijing 100083

Abstract:The structure of hot corrosion cell was changed with the increasing of porous oxides in products during the process of hot corrosion,it was macro cell that took main role in the direction vertical to the surface of samples.Anode reaction took place at the metal/compact oxide film interface,cathode reduction reaction took place at the molten salt+porous oxide/gas interface.The interfaces of porous oxide+molten salt/gas and metal+compact oxide film/molten salt were simulated,the acidity and basicity and oxygen activity were measured at both interfaces with time.It was shown that the gradient of basicity was positive in the salt film.The oxygen activity was decreased at the metal+compact oxide film/molten salt interface with time.

 

Key words: macro cell; basicity gradient; oxygen activity

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn