INVESTIGATION ON THE INTERFACE PHASE BY TEM IN A NEWLY DEVELOPED NEAR α TITANIUM ALLOY
Mao Pengling1; Xu Jialong1;Deng Yongrui2

1.Shanghai Iron & Steel Research Institute; Shanghai 200940;
2.University of Science and Technology Beijing; Beijing 100083)
Abstract:The interface phase(IFP) in a newly developed nearαtitanium alloy Ti-5l23 was investigated by TEM.The interface phase was not found after quenching and subsequent aging at below 800℃.After aging at 800℃,the interface phase appeared atα/β boundaries.The M layer of the interface phase was showed to be an fcc and its orientation relationship may be expressed as(001)m(110)βand[110]m.The S layer of the interface phase was showed to possess hexagonal and twin related on{1011},1012〉to the α.The element concentration gradient produced by diffusion at the boundaries under proper heating and cooling led to change of electron concentration,which probably was the main factor to create the interface phase in the titanium alloys.

Abstract:The interface phase(IFP) in a newly developed nearαtitanium alloy Ti-5l23 was investigated by TEM.The interface phase was not found after quenching and subsequent aging at below 800℃.After aging at 800℃,the interface phase appeared atα/β boundaries.The M layer of the interface phase was showed to be an fcc and its orientation relationship may be expressed as(001)m(110)βand[110]m.The S layer of the interface phase was showed to possess hexagonal and twin related on{1011},1012〉to the α.The element concentration gradient produced by diffusion at the boundaries under proper heating and cooling led to change of electron concentration,which probably was the main factor to create the interface phase in the titanium alloys.

 

Key words: titanium alloy interface phase electron concentration

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn