Debinding and sintering of warm compacted and
binder-treated complex iron-base part
NGAI Tonga Leo(倪东惠), ZHOU Sho-Bond(周水波), XIAO Shiny(肖志瑜), LI Yuan-Yuan(李元元)

Guangdong Key Laboratory for Advanced Metallic Materials Fabrication and Forming,
School of Mechanical Engineering, South China University of Technology, Guangzhou 510640, China

Abstract:Regular elemental powders were used in warm flow compaction instead of the expensive micron-sized powders to fabricate cross-shaped parts. Debinding behaviors, sintering properties and shape consistency of the sintered parts were studied. Binder removal was accomplished by heating green compacts at intermediate temperatures with optimal heating rates until the debinding temperature was reached. Results show that by controlling debinding process, complex parts with good shape consistence can be obtained by warm compaction of binder-treated powder. Fine and shiny surface was obtained and no surface defect can be observed for sintered parts debinded at 2 ℃/min, while defect can be observed in sintered parts debinded at 4 ℃/min.

 

Key words: binder-treated powder; warm compaction; debinding; complex powder metallurgy part

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn