Microstructures and properties of 1.0%Al2O3/Cu composite treated by rolling
LIU Xiang-bing(刘向兵)1, JIA Cheng-chang(贾成厂)1, CHEN Xiao-hua(陈晓华)1, GAI Guo-sheng(盖国胜)2

1. Powder Metallurgy Institute, University of Science and Technology Beijing, Beijing 100083, China;
2. Department of Materials Science and Engineering, Tsinghua University, Beijing 100084,China

Abstract:The 1.0%Al2O3/Cu (mass fraction) composite was prepared by hot pressing (HP), then treated by rolling to get a full density. The microstructures and the micro area element distribution of the composite were analyzed by SEM. The density, electric conductivity and tensile strength were also investigated. The experimental results show that the alumina particles are more dispersed and become smaller through a single-pass rolling. The pore existing in the composite is eliminated or closed under the rolling force. The relative density increases from 98.4% to 99.2%. The electric conductivity increases from 88.9%IACS to 91.2%IACS. The tensile strength is increased by 47% from 300 MPa to 440 MPa.

 

Key words: Al2O3/Cu composite; hot pressing; rolling; pores

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn