Electro-magnetism of peg-20000 doped with
nano-cobalt ferrite oxide powder containing La3+
XIAO Li(肖  利)1, 2, FANG Zheng(方  正)2, QIU Guan-zhou(邱冠周)3, LIU Jian-she(柳建设)3

1. Hunan Metallurgic Professional Technical College, Zhuzhou 412000, China;
2. School of Chemistry and Chemical engineering, Central South University, Changsha 410083, China;
3. School of Resources Processing and Bioengineering, Central South University, Changsha 410083,China

Abstract:The sol-gel method was used to prepare three kinds of nanometer magnetic particles, such as the nano-cobalt ferrite oxide powders and those doped by LaCl3∙nH2O. In the thermo-decomposition process of the precursors to get these magnetic particles, TG/DTG was applied to investigate their character. The prepared magnetic particles with average diameter less than 100 nm were characterized by XRD and TEM. The results show the difference between the activation energies of these particles in different thermo-decomposition stages, even not in the same stage for different samples. The cobalt ferrite doped with La3+ affects its saturation magnetization(ms) and coercive force(Hc). As CoCl2∙6H2O is partly substituted by La3+, the value of Hc decrease with the increase of ms. When FeCl2∙4H2O is partly substituted by La3+, Hc increases obviously. The three kinds of nanometer magnetic particles were doped into polyethylene glycol-20000 (peg-20000) with different ratios respectively to obtain compound substance with optimal conductivity of 0.686 S/m.

 

Key words: nanometer particle; thermo-decomposition process; magnetism; conductivity; polymer films

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn