Deposition of chromium aluminum nitride coatings by arc ion plating
ZHANG Shu-juan(张淑娟)1, LI Ming-sheng (李明升)1, FENG Chang-jie(冯长杰)2,
LIU Ting-zhi(刘庭芝) 1, DUO Shu-wang(多树旺) 1

1. Jiangxi Key Laboratory of Surface Engineering, Jiangxi Science and Technology Normal University,
Nanchang 330013, China;
2. Department of Materials Science and Engineering, Nanchang Institute of Aeronautical Technology,
 Nanchang 330063, China

Abstract:Cr-Al-N ternary coatings were deposited by arc ion plating method using isolated Cr target and Al target. The influence of AlN content on the phase change was studied by synthesizing Cr1−xAlxN coatings with different x values. The effects of substrate negative bias on the surface morphology, deposition rate and phase structure were investigated. As the aluminum content increases, the structure of (Cr1−xAlx)N changes from B1(NaCl) phase to B4(wurtzite) phase. The critical content of AlN solubilized in B1(NaCl) lattice is close to 0.7. With the increasing pulse negative bias, the deposition rate decreases constantly, the droplet contamination is more serious, the ion-etching effect on coating surface is more obvious, and the change of preferred orientation and the shift of XRD peak take place.

 

Key words: chromium aluminum nitride; arc ion plating; phase change; pulse bias

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn