Oxidation resistance of (Ti,Al,Cr)N coatings at 800 ℃
LI Ming-sheng (李明升)1, FENG Chang-jie(冯长杰)2, YANG Gan-lan(杨干兰)1,
HE Xiang-ming(何向明)1, LI Wen-kui(李文魁)1, XIANG Jun-huai(向军

1. Jiangxi Key Laboratory of Surface Engineering, Jiangxi Science and Technology Normal University,
Nanchang 330013, China;
2. Department of Materials Science and Engineering, Nanchang Institute of Aeronautical Technology,
Nanchang 330063, China

Abstract:The composite metastable (Ti0.5Al0.5)N, (Ti0.45Al0.45Cr0.1)N and (Ti0.35Al0.35Cr0.3)N coatings were respectively deposited on a wrought martensite steel 1Cr11Ni2W2MoV for aero-engine compressor blades by arc ion plating technique with pulse substrate bias. All the coatings have B1NaCl phase with a (200) preferred orientation and dense structures. The results show that the introduction of Cr into (Ti,Al)N gives rise to a minute shrinkage of crystal lattice. The incorporation of chromium into the coatings dramastically improves the oxidation-resistance of the coatings. For (Ti0.5Al0.5)N, a layered oxide scale forms after 100 h oxidation and the outer layer is the blend oxide of TiO2 and Al2O3, and the middle layer is rich in Al and the inner layer is rich in Ti. For (Ti0.45Al0.45Cr0.1)N, the oxide scale possesses a double-layered structure and the outer layer is rich in Ti. For (Ti0.35Al0.35Cr0.3)N, a Cr-rich compound oxide scale of Ti, Al and Cr forms, and a out-diffusion of Fe from steel to the nitride coating and oxide film during the oxidation takes place.

 

Key words: (Ti,Al,Cr)N; oxidation resistance; arc ion plating

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn