Corrosion behaviors of Cr-Al-N coatings deposited by
 reactive magnetron sputtering
DUO Shu-wang(多树旺)1, 2, ZHU Ming(朱  明)2, 3, LIU Ting-zhi(刘庭芝)1,
 LI Zhong-jun(李忠峻)1, WANG Peng(王  鹏)1, LI Mei-s

1. Jiangxi Key Laboratory of Surface Engineering, Jiangxi Science and Technology Normal University,
Nanchang 330013, China;
2. Department of Materials Science and Engineering, Xi’an University of Science and Technology,
Xi’an 710054, China;
3. Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

Abstract:CrN and Cr-Al-N coatings were deposited by reactive magnetron sputtering on the glass substrate, and their corrosion behavior was studied. The electrochemical tests using both DC (polarization curves) and AC techniques (EIS) were carried out on Potentiostat/Galvanstat (EG&G) in 3.5% (mass fraction) NaCl solution. After immersed into NaCl solution for 1 h, the mass of the CrN coating keeps constant with the time continuing. This can be explained by the passivation of the coating. The comparison between the corrosion potential (φcorr) of the Cr-Al-N coatings with different aluminum contents reveals that the corrosion potentials of the aluminum contain coatings are nobler than that of the CrN coatings. This means that the addition of aluminum shifts the corrosion potential to more positive potential value. Among these coatings, CrN in NaCl solution exhibits the worst corrosion resistance, while the corrosion resistance of Cr0.63Al0.37N in NaCl solution is the best. The polarization data and EIS data suggest that addition of aluminum can improve the corrosion resistance of CrN coating.

 

Key words: Cr-Al-N coatings; corrosion behavior; magnetron sputtering

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn