Microstructure and properties of unleaded free-cutting
brass containing stibium
XIAO Lai-rong(肖来荣)1,2, SHU Xue-peng(舒学鹏) 1,2, YI Dan-qing(易丹青)1,2,
 ZHANG Xi-min(张喜民) 1,2, QIN Jing-li(覃静丽) 1,2, HU J

1.School of Materials Science and Engineering, Central South University, Changsha 410083, China;
2.The Key Laboratory of Non-ferrous Metals, Materials Science and Engineering, Ministry of Education;
Changsha 410083; China

Abstract:A new environmental friendly cutting brass containing stibium instead of lead was produced by casting and rolling. The microstructure was observed and the mechanical, dezincification and cutting properties were studied. The results show that the white particles distribute in both grains and grain boundaries, and the particles are mainly intermetallics containing stibium. The tensile strength, yield strength and elongation percentage of half-hard Sb-brass is 461.72 MPa, 213.3 MPa and 15.67%, respectively. Corresponding to HPb59-1 by the size as well as appearance of the chips and the mechanism of free-cutting, the cutting property of unleaded free-cutting Sb-brass is excellent. The unleaded Sb-brass has excellent dezincification corrosion resistance, and the average depth of longitudinal section is about 295.4 μm, while the average depth of lateral section is about 214.7 μm, and it is feasible to develop a new unleaded free-cutting Sb-brass

 

Key words: nonleaded; free-cutting brass; stibium; microstructure; property

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn