Preparation of Ni/C core-shell composite powders by electroless plating method
ZHANG Hai-jun (张海军)1, LIU Yun (刘  云)1, JIA Quan-li(贾全利) 1, JIA Xiao-lin(贾晓林)2

1. Institute of High Temperature Ceramics, Zhengzhou University, Zhengzhou 450052, China;
2. College of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450052, China

Abstract:Ni/C core-shell composite powders were prepared by electroless nickel-plating. The effects of concentration of NiSO4, bathing temperature, ratio of hydrazine hydrate to NiSO4, pH of the solution, amounts of complexing reagent and surfactant, bath load of activated carbon and reaction time, and so on, on the preparation of Ni/C core-shell composite powders were studied. The results show that the principal factors for Ni/C composite powders preparation are bathing temperature, ratio of hydrazine hydrate to NiSO4 and pH of the solution. The optimum conditions are plating at 90 ℃ with pH10.7 and molar ratio of N2H4×H2O to Ni2+of 3.0. The plated nickel powders are observed to be sphere-like in morphology with size about 100 nm. The maximum dielectric loss of Ni/C core-shell composite powders is about 0.35, and its magnetic loss was low with value about 0 in 2−16 GHz.

 

Key words: Ni/C; core-shell powders; electroless plating; preparation

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn